Application: | Aviation, Electronics, Industrial, Chemical |
---|---|
Standard: | GB, ASTM |
Purity: | 85%-97% |
Alloy: | Alloy |
Shape: | Round |
Type: | Tungsten Ball |
Customization: |
---|
Suppliers with verified business licenses
AMS-T-21014 | Class 1 | Class 1 | Class 2 | Class 2 |
Composition |
90W7Ni3Fe | 91W6Ni3Fe | 92W5Ni3Fe | 93W4Ni3Fe |
(g/cm3) Density (g/cm3) |
17.1±0.15 | 17.25±0.15 | 17.50±0.15 | 17.60±0.15 |
Heat Treatment |
Sintering | Sintering | Sintering | Sintering |
(MPa) Tensile Strength (MPa) |
900-1000 | 900-1000 | 900-1100 | 900-1100 |
(%) Elongation (%) |
18-29 | 17-27 | 16-26 | 16-24 |
(HRC) Hardness(HRC) |
24-28 | 25-29 | 25-29 | 26-30 |
AMS-T-21014 | Class 3 | Class 3 | Class 3 |
Composition |
95W3Ni2Fe | 96W3Ni1Fe | 97W2Ni1Fe |
(g/cm3) Density (g/cm3) |
18.10±0.15 | 18.30±0.15 | 18.50±0.15 |
Heat Treatment |
Sintering | Sintering | Sintering |
(MPa) Tensile Strength (MPa) |
920-1100 | 920-1100 | 920-1100 |
(%) Elongation (%) |
10-22 | 8-22 | 6-13 |
(HRC) Hardness(HRC) |
27-32 | 28-34 | 28-36 |
Grades |
Mil-T-21014 | |||||
Class1 | Class1 | Class2 | Class3 | Class3 | Class4 | |
Composition |
90W6Ni4C u |
90W7Ni3Fe | 92.5W5.25Ni 2.25Fe |
95W3.5N i1.5Cu |
95W3.5N i1.5Fe |
97W2.1N i0.9Fe 18.5;0.66 8 |
(gm/cc;lbs/in 3) Density(gm/c |
17;0.614 | 17;0.614 | 17.5;0.632 | 18;0.65 | 18;0.65 |
c;lbs/in3) | ||||||
(HRC) Hardness(HR C) |
24 | 25 | 26 | 27 | 27 | 28 |
(PSI) Ultimate tension (PSI) |
110,000 | 120,000 | 114,000 | 110,000 | 120,000 | 123,000 |
2% (PSI) yield strength 2% deviation(PS I) |
80,000 | 88,000 | 114,000 | 110,000 | 120,000 | 123,000 |
(% in1″ ) Elongation( % in1″ ) |
6 | 10 | 7 | 7 | 7 | 5 |
(PSI) Proportional elastic limit(PSI) |
45,000 | 52,000 | 46,000 | 45,000 | 44,000 | 45,000 |
Magnetism |
No data |
Micro-mag netic |
Micro-magne tic |
No data |
Micro-ma gnetic |
Micro-ma gnetic |
ASTM-B-45 9-67 |
Grade1 Type && |
Grade1 Type && |
Grade2 Type&& |
Grade3 Type && |
Grade3 Type && |
Grade4 Type && |